  • China wholesale China Ts16949 Certificated Rare Earth Permanent Neodymium/AlNiCo/Ferrite Magnet or Cow

    Short Description:

    Hard ferrites based on barium ferrite and strontium powders (chemical formula BaO • 6Fe2O3 and SrO • 6Fe2O3) manufactured. They consist of oxidized metals, thus included in the ceramic materials group. They consist of approx. 90% iron oxide (Fe2O3) and 10% alkaline earth oxide (BaO or SrO) – raw materials which are plentiful and inexpensive. They divide into isotropic and anisotropic, the particles of the latter are aligned in a single
    direction which obtaining better magnetic characteristics. Isotropic magnets are shaped by compressing while anisotropic magnets are compressed within a magnetic field. This provides the magnet with a preferential direction and triples its energy density.


    Product Detail

    Product Tags

    We believe that long expression partnership is often a result of top of the range, value added service, prosperous encounter and personal contact for China wholesale China Ts16949 Certificated Rare Earth Permanent Neodymium/AlNiCo/Ferrite Magnet or Cow, We’ve been not pleased while using the present achievements but we are trying finest to innovate to satisfy buyer’s much more personalized needs. No matter where you will be from, we have been here to wait for your sort ask for, and welcom to go to our manufacturing facility. Choose us, you can meet your trusted supplier.
    We believe that long expression partnership is often a result of top of the range, value added service, prosperous encounter and personal contact for China Cow Magnet, Ferrite Magnet, Our products are widely sold to Europe, USA, Russia, UK, France, Australia, Middle East, South America, Africa, and Southeast Asia, etc. Our solutions are highly recognized by our customers from all around the world. And our company is committed to continually improving effectiveness of our management system to maximize customer satisfaction. We sincerely hope to make progress with our customers and create a win-win future together. Welcome to join us for business!
    Introduction:
    Hard ferrites based on barium ferrite and strontium powders (chemical formula BaO • 6Fe2O3 and SrO • 6Fe2O3) manufactured. They consist of oxidized metals, thus included in the ceramic materials group. They consist of approx. 90% iron oxide (Fe2O3) and 10% alkaline earth oxide (BaO or SrO) – raw materials which are plentiful and inexpensive. They divide into isotropic and anisotropic, the particles of the latter are aligned in a single
    direction which obtaining better magnetic characteristics. Isotropic magnets are shaped by compressing while anisotropic magnets are compressed within a magnetic field. This provides the magnet with a preferential direction and triples its energy density.
    Advantage:
    As is typical of oxide ceramics, hard ferrite magnets display relatively resistant behavior towards moisture, solvents, alkaline solutions, weak acids, salts, lubricants and gas pollutants. Generally, hard ferrite magnets can therefore be used without additional corrosion protection.
    Feature:
    Due to their great hardness (6-7 Mohs), Ferrite magnets are brittle and sensitive to knocks or bending. During processing, they have to be machined with diamond tools. Operating temperatures with ferrite magnets are generally between –40ºC and 250ºC.
    Application:
    Different shapes are used in utomotive engineering, such as automation and measurement control. Other applications such as Automobile electrical machinery (wipers, sit chair motor), Teaching, Door absorber, Magnetic bike and massage chair, etc.
    Today, hard ferrites represent the largest proportion of permanent magnets produced. In contrast to AlNiCo magnets, hard ferrites are characterized by flux densities but high coercive field strengths. This results in the generally flat shape of the materials. Barium ferrite and strontium ferrite are differentiated depending on the starting material. All stated values were determined using standard samples according IEC 60404-5. The following specifications serve as reference values and may differ.

    Sintered Ferrite Magnet Physical Properties
    Grade Remanence Rev. Temp.   Coeff. Of Br Coercive Force Intrinsic Coercive Force Rev. Temp.-Coeff. Of Hcj Max. Energy Product Max. Operating Temperature Density
    Br (KGs) Hcb (KOe) Hcj (KOe) (BH)max. (MGOe) g/cm³
    Y10T 2.0-2.35 -0.20 1.57-2.01 2.64-3.52 +0.30 0.8-1.2 250℃ 4.95
    Y20 3.2-3.8 -0.20 1.70-2.38 1.76-2.45 +0.30 2.3-2.8 250℃ 4.95
    Y22H 3.1-3.6 -0.20 2.77-3.14 3.52-4.02 +0.30 2.5-3.2 250℃ 4.95
    Y23 3.2-3.7 -0.20 2.14-2.38 2.39-2.89 +0.30 2.5-3.2 250℃ 4.95
    Y25 3.6-4.0 -0.20 1.70-2.14 1.76-2.51 +0.30 2.8-3.5 250℃ 4.95
    Y26H 3.6-3.9 -0.20 2.77-3.14 2.83-3.21 +0.30 2.9-3.5 250℃ 4.95
    Y27H 3.7-4.0 -0.20 2.58-3.14 2.64-3.21 +0.30 3.1-3.7 250℃ 4.95
    Y28 3.7-4.0 -0.20 2.20-2.64 2.26-2.77 +0.30 3.3-3.8 250℃ 4.95
    Y30 3.7-4.0 -0.20 2.20-2.64 2.64-2.77 +0.30 3.3-3.8 250℃ 4.95
    Y30H-1 3.8-4.0 -0.20 2.89-3.46 2.95-3.65 +0.30 3.4-4.1 250℃ 4.95
    Y30BH 3.8-3.9 -0.20 2.80-2.95 2.90-3.08 +0.30 3.4-3.7 250℃ 4.95
    Y30-1 3.6-4.0 -0.20 1.70-2.14 1.76-2.51 +0.30 2.8-3.5 250℃ 4.95
    Y30BH-1 3.8-4.0 -0.20 2.89-3.46 2.95-3.65 +0.30 3.4-4.0 250℃ 4.95
    Y30H-2 3.95-4.15 -0.20 3.46-3.77 3.90-4.21 +0.30 3.5-4.0 250℃ 4.95
    Y20-2 3.95-4.15 -0.20 3.46-3.77 3.90-4.21 +0.30 3.5-4.0 250℃ 4.95
    Y32 4.0-4.2 -0.20 2.01-2.38 2.07-2.45 +0.30 3.8-4.2 250℃ 4.95
    Y33 4.1-4.3 -0.20 2.77-3.14 2.83-3.21 +0.30 4.0-4.4 250℃ 4.95
    Y35 4.0-4.1 -0.20 2.20-2.45 2.26-2.51 +0.30 3.8-4.0 250℃ 4.95

    Note:
    · We remain the same as above unless specified from customer. Curie temperature and temperature coefficient are for reference only, not as a basis for decision.
    · The maximum working temperature of magnet is changeable due to ratio of length and diameter and environment factors.